Product Introduction
This product uses environmentally friendly water-based epoxy resin dispersion, which has high corrosion resistance, high hardness, convenient construction performance, super strong corrosion resistance, good substrate adhesion, high adhesion to various substrates, ultra-low VOC content, low odor and no pollution.Product Application
Anti corrosion coatings for metal components, ship coatings, engineering machinery, bridge and steel structure engineering, and industrial heavy anti-corrosion.Instructions
1. Surface treatment: Before painting, the surface of the substrate should be cleaned of oil stains, rust, and other dirt to ensure that the substrate is clean, dry, and free of pollution. Polish the welding slag on the metal surface until it is smooth, sandblasting to Sa2.5 level or manually polishing to St2 level. 2. Dilution ratio: Before construction, mix the original paint evenly, add curing agent and purified water in proportion, and stir while adding. After mixing evenly, let it sit for 3-5 minutes before construction. The mixed paint should be used up in about 4 hours. Please request detailed construction instructions from our company for the specific construction ratio. 3. Construction method and tools: This product is suitable for spraying. Maintain a dry and ventilated construction environment, with a recommended construction temperature of ≥ 5 ° C; Humidity ≤ 75% R.C.Storage and transportation
1. The product should be stored in a dry and ventilated place, with a storage temperature greater than 0 ° C~40 ° C, to prevent water immersion, and kept away from heat sources. 2. The storage period is 12 months. If it exceeds the storage period, it can be inspected and can still be used if it meets the standards. 3. Protect the product from rain, sun, and severe cold during transportation. It should comply with the regulations of the transportation department.| Project | Parameter detection | Standard |
| Color and appearance | grey | Visualization |
| Solid Content% | ≥80 | GB/T1725-2007 |
| zinc% | 70 | none |
| Fineness | ≤35 | GB/T675301-2007 |
| Hardness (pencil) | 2H | GB/T6739-2006 |
| Adhesion | Level 0 | GB/T1720-79(89) |
| FlexibilityMM | ≤3 | GB/T1731-79(93) |
| Impact resistanceKG/CM | 50 | GB/T1732-93 |
| Salt spray resistanceH | 无 | GB/T1771-2007 |
| Drying time(25℃)H | Surface0.5H | GB/T1728-79(89) |
| Drying time(25℃)H | Actual drying6H | GB/T1728-79(89) |