DESCRIPTION
This product is made of high-quality acrylic copolymerization lotion, natural granite rubble colored sand, imported additives, water and other advanced technologies. It is a kind of bright and delicate exterior wall decoration materialApplication
Widely used for coating exterior wall insulation surfaces and decorating and protecting high-end high-rise buildings, hotels, star rated hotels, civil buildings, villas and other buildings.Performance characteristics
1. Using natural granite crushed sand to showcase the color of real stone paint, maintaining color stability and never fading. 2. The paint film has excellent stain resistance, water resistance, alkali and acid rain resistance. 3. The decorated building has a luxurious and elegant effect, with a thick and hard coating.Precautions
1. Strictly follow the substrate treatment method to treat the surface and maintain sufficient curing time for the wall. 2. Due to the use of natural colored sand for color matching in this product, there may be slight color differences between different batches. Construction should ensure that the same batch of products is used on the same wall. 3. Suggest using other products provided by our company to ensure construction quality. 4. Diluted paint cannot be poured back into its original packaging; If it cannot be used up in one go after opening, it must be resealed in a timely manner. 5. This product should be stored in a cool, dry place away from light, with a shelf life of 6 months. Construction is not suitable when the temperature is below 5 ° C and above 40 ° C.Execution standards
JG/T24| Project | TECHNICAL INDEX |
| Main components | Acrylic acid copolymerization lotion, natural color sand, high-quality additives and water, etc |
| Status in container | After stirring, there are no lumps and it is in a uniform state |
| Surface drying time | ＜4h |
| Repainting interval | ≥8h |
| Theoretical Coverage | 2.5~3.5kg/㎡/time(Theoretical coating thickness：1.5~2mm) |
| Impact resistance | The coating has no cracks, peeling or obvious deformation |
| Water resistance (96h) | The coating has no bulging, cracking, or peeling phenomenon |
| Bonding strength(MPa)Standard state | 0.9~1.4 |
| Bonding strength(MPa)After immersion in water | 0.7~1.2 |
| Dirt collection 5 time | <Level 2 after 5 cycles of testing |
| Artificial aging resistance | 500h The coating has no cracking, bulging, peeling, powdering level 0, discoloration ≤ level 1 |
Note: 1. Drying time varies with temperature and humidity, with reference conditions of 25 ℃ and relative humidity<65%
2. The actual usage of the product varies due to different factors such as construction technology, coating thickness, and flatness.