DESCRIPTION
This product is made of advanced silica modified acrylic lotion, imported high-quality rutile titanium dioxide and high-quality additives. Due to the introduction of siloxane, during the film forming process of lotion, the silicon oxygen bond is hydrolyzed to form a dense interpenetrating three-dimensional network, which makes the film have unique water resistance and permeability, and can significantly improve the stain resistance, water resistance and durability of buildings.Application
Widely used for exterior wall decoration and protection of high-rise buildings, office buildings, hotels, government buildings, factories, schools, etc.Performance characteristics
1. Excellent stain resistance and scrub resistance. 2. High durability and long service life. 3. Has long-term anti mold and anti algae effects. 4. Strong adhesion and long-lasting coating that does not peel off.Construction technology
1. Base treatment: The base layer needs to be dry, clean, flat, and firm. Use flexible putty or polymer fine mortar with appropriate strength and good water resistance to scrape the base layer flat, usually 2-3 times; 2. Bottom coat construction: Roll or spray 1-2 coats of exterior wall specific primer on the putty layer or other substrate that meets the maintenance requirements; 3. Topcoat construction: After the primer dries, apply two coats of high weather resistance and stain resistant exterior wall paint by rolling or spraying.Precautions
1. Strictly follow the substrate treatment method to treat the surface and maintain sufficient curing time for the wall. 2. It is recommended to use other products provided by our company to ensure construction quality. 3. Diluted paint cannot be poured back into its original packaging; If it cannot be used up in one go after opening, it must be resealed in a timely manner. The dilution ratio of colored paint with water should not exceed 5%, and white paint can be diluted with water up to 15% of the ratio. 5. This product should be stored in a cool, dry place away from light, and has a shelf life of 12 months. Construction is not suitable when the temperature is below 5 ° C and above 40 ° C.Execution standards
GB/T9755 GB/T24408| Project | TECHNICAL INDEX |
| Main components | Silicon modified acrylic lotion, inorganic pigments and fillers, high-quality additives and water, etc |
| Status in container | After stirring, there are no lumps and it is in a uniform state |
| Surface drying time | ＜2h |
| Repainting interval | ≥6h |
| Theoretical Coverage | 8~12㎡/kg/time |
| Dirt collection | ＜10% |
| Washability | ＞8000times |
| Water resistance(96h) | The coating has no bulging, cracking, or peeling phenomenon |
| Artificial aging resistance | 1000h |
Note: 1. Drying time varies with temperature and humidity, with reference conditions of 25 ℃ and relative humidity<65%
2. The actual usage of the product varies due to different factors such as construction technology, coating thickness, and flatness.